信息類型：供應

??深圳鈑金加工廠鈑金加工展開圖是依據零件圖（3D）展開的平面圖（2D）1．展開方式要合，要便利節省材料及加工性2．合理選擇間隙及包邊方式，T=2.0以下問隙0.2，T=2-3問隙0.5，包邊方式采用長邊包短邊（門板類）3．合理考慮公差外形尺寸：負差走到底，正差走一半；孔形尺寸：正差走到底，負差走一半。The sheet metal processing unfolding drawing is based on the part drawing (3D) unfolding plan (2D) 1. The unfolding method should be suitable, and the material and workability should be saved conveniently. 2. Reasonable **ion of clearance and edge wrapping mode, T = 0.2 below 2.0, T = 2-3, 0.5, the edge wrapping mode adopts the long edge wrapping short edge (door type) 3. Reasonable consideration of tolerance shape size: negative. The difference between the right and the wrong is half the hole size.4．毛刺方向4. burr direction5．抽牙、壓鉚、撕裂、沖凸點（包），等位置方向，畫出剖視圖5. draw teeth, press riveting, tearing, bump bump (package), etc. position direction, draw sectional view.6．核對材質，板厚，以板厚公差6. check material, plate thickness, thickness tolerance.7．特殊角度，折彎角內半徑（一般R=0.5）要試折而定展開7. special angle, the radius of the bending angle (general R=0.5) should be measured and expanded.8．有易出錯（相似不對稱）的地方應重點提示8. where there is error prone (similar asymmetry), we should give priority to hints.9．尺寸較多的地方要加放大圖9. larger size should be enlarged.10． 需噴涂保護地方須表示10. spray protection must be indicated.加工流程Processing flow根據鈑金件結構的差異，工藝流程可各不相同，但總的不超過以下幾點。According to the difference of sheet metal structure, the process flow can be different, but the total does not exceed the following points.1、下料：下料方式有各種，主要有以下幾種方式1. Blanking: there are various ways of cutting materials, mainly in the following ways.①． 剪床：是利用剪床剪切條料簡單料件，它主要是為模具落料成形準備加工，成本低，精度低于0.2，但只能加工無孔無切角的條料或塊料。(1) Shearing machine: shearing bars with shearing machine is a simple material, it is mainly prepared for die blanking forming, low cost, accuracy is lower than 0.2, but can only process bars or blocks without holes and cutting angles.②． 沖床：是利用沖床分一步或多步在板材上將零件展開后的平板件沖裁成形各種形狀料件，其優點是耗費工時短，效率高，精度高，成本低，適用大批量生產，但要設計模具。(2) Punching machine: It is the use of one-step or multi-step punching on the sheet metal parts after the expansion of various shapes of blanks, its advantages are time-consuming, high efficiency, high precision, low cost, suitable for mass production, but to design the mold.③． NC數控下料，NC下料時首先要編寫數控加工程式，利用編程軟件，將繪制的展開圖編寫成NC數拉加工機床可識別的程式，讓其根據這些程式一步一刀在平板上沖裁各構形狀平板件，但其結構 受刀具結構所至，成本低，精度于0.15。NC NC blanking, NC blanking first to write NC machining program, the use of programming software, the drawing of the expansion diagram into NC number drawing machine tools can identify the program, so that according to these programs one by one tool blanking on the flat plate with various structural shapes, but its structure by the tool structure, low cost, precision in 0.15.④． 鐳射下料，是利用激光切割方式，在大平板上將其平板的結構形狀切割出來，同NC下料一樣需編寫鐳射程式，它可下各種復雜形狀的平板件，成本高，精度于0.1.Laser cutting is to use laser cutting method to cut out the structural shape of its flat plate on a large plate. Like NC cutting, it needs to write laser program. It can lower various complex shape of flat parts with high cost and accuracy of 0.1.⑤． 鋸床：主要用下鋁型材、方管、圖管、圓棒料之類，成本低，精度低。Sawing machine: mainly use lower aluminum profile, square tube, picture tube, round bar material and so on, with low cost and low precision.1． 鉗工:沉孔、攻絲、擴孔、鉆孔1. fitter: hole sinking, tapping, reaming and drilling.沉孔角度一般120℃，用于拉鉚釘，90℃用于沉頭螺釘，攻絲英制底孔。The hole sinking angle is usually 120 degrees, which is used for pulling rivets, 90 degrees for countersunk screws, and for British bottom holes.2． 翻邊：又叫抽孔、翻孔，就是在一個較小的基孔上抽成一個稍大的孔，再攻絲，主要用板厚比較薄的鈑金加工，增加其強度和螺紋圈數，避免滑牙，一般用于板厚比較薄，其孔周正常的淺翻邊，厚度基本沒有變化，允許有厚度的變薄30-40%時，可得到比正常翻邊高度大高40-60%的高度，用擠薄50%時，可得的翻邊高度，當板厚較大時，如2.0、2.5等以上的板厚，便可直接攻絲。2. Flanging: also known as hole pulling, hole turning, is in a smaller hole on the base of a slightly larger hole, and then tapping, mainly thin sheet metal processing, increase its strength and the number of threads to avoid sliding teeth, generally used for thin plate thickness, its hole normal shallow flanging, thickness basically unchanged, allowing thickness The maximum flanging height can be obtained when the flanging height is 40-60% higher than the normal flanging height when the flanging thickness is 30-40% thinner. The maximum flanging height can be obtained when the flanging height is 50% thinner. When the plate thickness is large, such as 2.0, 2.5 or more, it can be tapped directly.3． 沖床：是利用模具成形的加工工序，一般沖床加工的有沖孔、切角、落料、沖凸包（凸點），沖撕裂、抽孔、成形等加工方式，其加工需要有相應的模具來完成操作，如沖孔落料模、凸包模、撕裂模、抽孔模、成型模等，操作主要注意位置，方向性。3. Punching machine: is the use of mold forming processing procedures, the general punch processing has punching, cutting angle, blanking, punching bump (bump), punching and tearing, hole drawing, forming and other processing methods, its processing needs to complete the operation of the corresponding mold, such as punching and blanking die, punching and blanking die, punching die, tearing die, punching die, forming die, etc., operation. Take the main position and direction.4． 壓鉚：壓鉚就本公司而言，主要有壓鉚螺母、螺釘、松不脫等，其是通過液壓壓鉚機或沖床來完成操作，將其鉚接到鈑金件上，還有漲鉚方式，需注意方向性。4. Pressure riveting: Pressure riveting as far as the company is concerned, mainly riveting nuts, screws, loose, etc., which is through the hydraulic press riveting machine or punch to complete the operation, riveting it to the sheet metal, and riveting way, need to pay attention to the direction.5． 折彎；折彎就是將2D的平板件，折成3D的零件。其加工需要有折床及相應折彎模具完成，它也有一定折彎順序，其原則是對下一刀不產生干涉的先折，會產生干涉的后折。5. bending; bending is to turn the flat parts of 2D into 3D parts. Its processing needs a folding bed and the corresponding bending die to complete, it also has a certain order of bending, the principle is that the next knife does not interfere with the first bending, will produce interference after the folding.l 折彎條數是T=3.0mm以下6倍板厚計算槽寬，如：T=1.0、V=6 .0 F=1.8、T=1.2、V=8、F=2.2、T=1.5、V=10、F=2.7、T=2.0、V=12、F=4.0 l 折床模具分類，直刀、彎刀（80℃、30℃）The number of bending strips is 6 times the width of calculation slot of plate thickness below T = 3.0mm, such as: T = 1.0, V = 6.0F = 1.8, T = 1.2, V = 8, F = 2.2, T = 1.5, V = 10, F = 2.7, T = 2.0, V = 12, F = 4.0L bending die classification, straight knife, bending knife (80 ~30 ~C)l 鋁板折彎時，有裂紋，可增加下模槽寬式增加上模R（退火可避免裂紋）When the L aluminum plate is bent, there is a crack. The lower die groove can be added to increase the width of the upper die R (annealing can avoid cracks).l 折彎時注意事項：Ⅰ圖面，要求板材厚度，數量； Ⅱ折彎方向L points for attention when bending: I. surface, thickness, quantity, and bending direction.Ⅲ折彎角度；Ⅳ折彎尺寸；Ⅵ外觀、電鍍鉻化料件不許有折痕。Bending angle; IV bending size; VI appearance, chrome plating materials are not allowed to crease.折彎與壓鉚工序關系，一般情況下先壓鉚后折彎，但有料件壓鉚后會干涉就要先折后壓，又有些需折彎—壓鉚—再折彎等工序。Bending and riveting process relationship, in general, first riveting before bending, but the material will interfere with riveting after bending, and some need to bend - riveting - bending and other processes.以上就是深圳鈑金加工廠加工的注意事項與加工流程，詳細可訪問貴喜鈑金加工有限公司www.sz-banjin.cn